Excessive Orange Peel
Adjust film thickness to recommended range.
Lower the voltage settings on the equipment.
Some powder coatings are formulated and manufactured to tighter, more controlled particle size distribution allowing for a smoother film.
Inadequate Film Thickness
Increase voltage setting.
Adjust gun placement closer to the part and try different nozzles.
Adjust part density (racking) so that powder can be attracted equally to each part.
Excessive air velocity may be blowing powder past the part.
Poor grounding. Check your hooks.
Excessive humidity may limit the charge on the powder particles.
Powder may be too fine. Always maintain a consistent blend of virgin and recycled powder. Contact your KRIPTON Technical Service Representative for a particle size analysis.
Some powder technologies charge better or are meant to be applied as thin films. Contact your KRIPTON Technical Service Representative.
Back Ionization
Back ionization occurs when powder layers start being repelled from the part during application.
Turn voltage settings down.
Excessive powder build up can cause back ionization. Lower powder feed rates and adjusts gun distances.
Having gun too close to the part.
Poor Fluidization in Hopper
Check your fluidizing membrane for plugged pores. Can be caused by moisture or oil in the air supply.
Increase air pressure to fluidizer.
Check for packed powder by stirring manually with a paddle or air.
Powder Blowing Out of Hopper
Lower air pressure in fluidizing hopper.
Powder may be too fine. Consult KRIPTON Technical Service Representative for a particle size analysis.
Check hopper for proper venting.
Geysering
Geysering is caused by air blowing holes through the surface of the fluidized powder.
Lower air pressure to the fluidizer.
Add more powder. Hopper should be about 3⁄4 full when fluidizing.
Check for plugged pores or other obstructions in membrane.
Powder may be packed or moist. Check air supply for contaminants.
Impact Fusion
Impact Fusion is the hard build up of powder particles that occur in hoses, tubes and nozzles. Clean and replace tubes, hoses, venturi pumps and nozzles on a regular basis.
Powder may be too fine. Reduce your reclaim.
Excessive air pressures and powder feed rates will increase the amount of impact fusion.
Check air supply for contaminants.
Surging or Inconsistent Powder Flow
Increase air pressure and/or volume of air.
Check powder hoses for kinks or obstructions. Keep hose length to a minimum. May need to replace powder hose with a smaller inside diameter hose.
Clean all tubes, hoses and guns of impact fusion build up.
Check powder delivery and air pressure settings.
Check hopper for powder level and fluidization.
Check air supply for contaminants.
Excessive temperature and humidity in application area can cause application problems.
Check for sintering or clumping in powder.
Surging or Inconsistent Powder Flow
Poor Spray Patterns or Powder Feed
Replace worn feed tubes, orifices, and deflectors in spray guns.
Clean impact fusion from areas of accumulation.
Increase powder feed (see notes in "Inconsistent Flow" section)
Choose correct nozzle for part configuration.
Check air supply for contaminants.
Excessive temperature and humidity in application area can cause application problems.
Check for sintering or clumping in powder.
Powder Drift From Spray Booth
Clean or replace filter cartridges and final filters.
Check pulse air pressure and for contaminants in air supply.
Excessive drafts or pressure from outside the spray area causing turbulence.
Using excessive amounts of compressed air during clean up.
Insufficient air volume or velocity in recovery/reclaim.
Excessive amount of fines.
If guns are added to a booth or flows are run at their maximum it may exceed the filter surface capacity and lead to powder migration out of the booth. Decrease flow rates.
Spitting and Dry Spray of Metallics
Spitting is caused by particles collecting on the diffuser and electrode.
Periodically clean the electrode with air and adjust KV’s and powder delivery.
To reduce dry spray, adjust KV’s and lower delivery volume and powder velocity.
Control film thicknesses for more consistent color.
Check KV Output at the gun.